Journal Article

IMPULSE-2022-00138

http://join2-wiki.gsi.de/foswiki/pub/Main/Artwork/join2_logo100x88.png Thermal properties of U-Mo alloys irradiated under high fission power density

Burkes, D. E. ; Schwerdt, I. J. ; Huber, T. ; Breitkreutz, H. ; Reiter, C.MLZ* ; Petry, W.MLZ* ; Schulthess, J. L. ; Casella, A. M. ; Casella, A. J. ; Buck, E. C. ; Pool, K. N. ; MacFarlan, P. J. ; Edwards, M. K. ; Smith, F. N.

2021
Elsevier Science Amsterdam [u.a.]

Please use a persistent id in citations: doi:10.1016/j.jnucmat.2021.152823

Abstract: A variety of physical and thermal property measurements made on irradiated U-Mo alloy monolithic fuel samples with a Zr diffusion barrier and clad in Al alloy 6061 are reported. These properties form the basis for additional investigations in thermal behavior of U-Mo fuel under high performance research reactor irradiation conditions. Measurements were performed on samples harvested from fuel plates irradiated under high fission power density and surface heat flux and complement previous measurements on samples subjected to moderate fission power density and surface heat flux. Sample measurements reported in this work represented fission density ranging from 2.42 – 4.81 × 1027 fissions•m−3 (20.8 – 36.5 235U depletion) and average plate surface temperatures from 355 – 414 K. Specific heat capacity of irradiated monolithic U-Mo increases with increasing temperature and fission density, but carries large uncertainties associated with thickness measurements used to determine the mass fraction of the layer constituents for extraction of the U-Mo specific heat capacity, specifically the very thin and nonuniform Zr diffusion barrier. Density of irradiated monolithic U-Mo decreases with increasing fission density resulting from fission gas swelling and porosity formation. Thermal diffusivity of irradiated monolithic U-Mo increased with increasing temperature and decreased with increasing fission density. Thermal conductivity of irradiated monolithic U-Mo increased with increasing temperature, and in general, appeared to decrease and become less sensitive to temperature with increasing fission density. Thermal conductivity measurements compared to a semi-empirical model agreed within ±30%. It is suspected that the main driver in deviation between model calculations and measurements is the fission gas swelling determination, which does not account for fission power density or irradiation temperature.

Keyword(s): Engineering, Industrial Materials and Processing (1st) ; Industrial Application (2nd) ; Materials Science (2nd)

---

Contributing Institute(s):

1. CNSI (RPHYSICS ; CNSI)
2. CNSI-LABS (HEUMEULAB ; CNSI-LABS)

Experiment(s):

1. HEU-MEU: Brennstoffentwicklung

---

Database coverage:
; Clarivate Analytics Master Journal List ; Current Contents - Engineering, Computing and Technology ; Current Contents - Physical, Chemical and Earth Sciences ; Ebsco Academic Search ; Essential Science Indicators ; IF < 5 ; JCR ; Nationallizenz ; SCOPUS ; Science Citation Index Expanded ; Web of Science Core Collection

---